XXHD01
XINXING
XINXING can produce all kinds of HDPE Sheets as per cutomer demands. Single color HDPE Sheets, dual color HDPE Sheets, glossy HDPE Sheets, textured HDPE Sheets. Thickness from 1mm -200mm
Polyethylene PE500 PE 300 sheet /board/plate - HMWPE offers increased wear resistance and impact strength compared to HDPE. It is extremely strong, has excellent resistance to chemicals and low temperatures and has very low moisture absorption. Polyethylene PE300 PE500 sheet
Application
Buffers, cutting boards, chopping boards, change parts and protection strips.
Key Features
• Temperature: -100°C up to +80°C (+100°C short term).
• High impact strength and resistance to shock.
• Excellent resistance to chemicals and low temperatures.
• Good electrical insulation properties.
• Excellent non-stick properties.
• Low moisture absorption.
• Food approved.
Size and color
Any color is available
Data sheet
Mechanical Properties | Value | Unit | DIN/EN/SO | |
Tensile strength at yield | 25 | MPa | 527/D638 | |
Elongation at Break | 300 | % | 527 | |
Modulus of elasticity in tension | 1000 | MPa | 527/D638 | |
Modulus of elasticity in flexure | 1000-1400 | MPa | 178/D790 | |
Impact strength | 15 | kJ/m² | 179/D256 | |
Creep rupture strength after 1000hrs with static load | 12.5 | MPa | - | |
Time yield limit for 1% elongation after 1000hrs | 3 | MPa | - | |
Coefficient of friction against hardened and ground steel P= 0.05 N/mm2, v= 0.6m/s | 0.29 | - | - | |
Ball indentation hardness | 43 | MPa | 2039-1 | |
Shore hardness D | 64 | - | 868 | |
Thermal Properties | Value | Unit | DIN/EN/ISO | |
Glass transition temperature | -95 | °C | 53736 | |
Crystalline melting point | 130 | °C | 53736 | |
Service temperature (short term) | 100 | °C | - | |
Service temperature (long term) | 80 | °C | - | |
Coefficient of thermal expansion | 13-15 | 10-5K | 53483/D696 | |
Specific heat | 1.7-2 | J/(g*K) | - | |
Coefficient of thermal conductivity | 0.35-0.43 | W/(K*m) | - | |
Electrical properties | Value | Unit | DIN/IEC | |
Surface resistivity | 1014 | Ohm | 60093 | |
Dielectric strength | 50 | kV/mm | 60243-1 | |
Other properties | Value | Unit | DIN/EN/ISO/IEC | |
Water absorption @ saturation @ 23°c | <0.05 | % | 62 | |
Resistance to hot water, washing soda | Resistant | - | - | |
Resistance to weathering | Yes | - | - | |
Flammability (UL94) | HB | - | - | |
Volume Resistivity UV Stabilized | D257 | Ohm-cm fine | >6X1015 | |
XINXING can produce all kinds of HDPE Sheets as per cutomer demands. Single color HDPE Sheets, dual color HDPE Sheets, glossy HDPE Sheets, textured HDPE Sheets. Thickness from 1mm -200mm
Polyethylene PE500 PE 300 sheet /board/plate - HMWPE offers increased wear resistance and impact strength compared to HDPE. It is extremely strong, has excellent resistance to chemicals and low temperatures and has very low moisture absorption. Polyethylene PE300 PE500 sheet
Application
Buffers, cutting boards, chopping boards, change parts and protection strips.
Key Features
• Temperature: -100°C up to +80°C (+100°C short term).
• High impact strength and resistance to shock.
• Excellent resistance to chemicals and low temperatures.
• Good electrical insulation properties.
• Excellent non-stick properties.
• Low moisture absorption.
• Food approved.
Size and color
Any color is available
Data sheet
Mechanical Properties | Value | Unit | DIN/EN/SO | |
Tensile strength at yield | 25 | MPa | 527/D638 | |
Elongation at Break | 300 | % | 527 | |
Modulus of elasticity in tension | 1000 | MPa | 527/D638 | |
Modulus of elasticity in flexure | 1000-1400 | MPa | 178/D790 | |
Impact strength | 15 | kJ/m² | 179/D256 | |
Creep rupture strength after 1000hrs with static load | 12.5 | MPa | - | |
Time yield limit for 1% elongation after 1000hrs | 3 | MPa | - | |
Coefficient of friction against hardened and ground steel P= 0.05 N/mm2, v= 0.6m/s | 0.29 | - | - | |
Ball indentation hardness | 43 | MPa | 2039-1 | |
Shore hardness D | 64 | - | 868 | |
Thermal Properties | Value | Unit | DIN/EN/ISO | |
Glass transition temperature | -95 | °C | 53736 | |
Crystalline melting point | 130 | °C | 53736 | |
Service temperature (short term) | 100 | °C | - | |
Service temperature (long term) | 80 | °C | - | |
Coefficient of thermal expansion | 13-15 | 10-5K | 53483/D696 | |
Specific heat | 1.7-2 | J/(g*K) | - | |
Coefficient of thermal conductivity | 0.35-0.43 | W/(K*m) | - | |
Electrical properties | Value | Unit | DIN/IEC | |
Surface resistivity | 1014 | Ohm | 60093 | |
Dielectric strength | 50 | kV/mm | 60243-1 | |
Other properties | Value | Unit | DIN/EN/ISO/IEC | |
Water absorption @ saturation @ 23°c | <0.05 | % | 62 | |
Resistance to hot water, washing soda | Resistant | - | - | |
Resistance to weathering | Yes | - | - | |
Flammability (UL94) | HB | - | - | |
Volume Resistivity UV Stabilized | D257 | Ohm-cm fine | >6X1015 | |